Para-amino benzoic acid–mediated synthesis of vaterite phase of calcium carbonate /
Ramesh, T.N.
Para-amino benzoic acid–mediated synthesis of vaterite phase of calcium carbonate / created by T.N. Ramesh, S.A. Inchara and K. Pallavi - Journal of chemical sciences Volume 127, number 5, .
Calcium carbonate polymorphs were precipitated at room temperature and 80∘C by varying the precipitation pH, carbonate source, effect of solvent in presence and absence of structure directing agent such as para-aminobenzoic acid. Calcite phase of calcium carbonate was obtained when sodium hydrogen carbonate and/or sodium carbonate (used as precipitating agents) were added to calcium chloride solution at different pHs in water and/or methanol as solvent in separate experiments. Vaterite phase of calcium carbonate (CaCO3) has been synthesized by mixing calcium chloride and sodium carbonate in presence of para-aminobenzoic acid when water–methanol binary mixture was used as solvent. Vaterite phase of calcium carbonate crystallizes in P63/mmc, while that of calcite phase in R-3mc, respectively. Calcite phase of calcium carbonate exhibits rhombohedral morphology, while vaterite phase has spherical morphology.
09743626
Calcium carbonate--Vaterite--Chemical synthesis
QD31 JOU
Para-amino benzoic acid–mediated synthesis of vaterite phase of calcium carbonate / created by T.N. Ramesh, S.A. Inchara and K. Pallavi - Journal of chemical sciences Volume 127, number 5, .
Calcium carbonate polymorphs were precipitated at room temperature and 80∘C by varying the precipitation pH, carbonate source, effect of solvent in presence and absence of structure directing agent such as para-aminobenzoic acid. Calcite phase of calcium carbonate was obtained when sodium hydrogen carbonate and/or sodium carbonate (used as precipitating agents) were added to calcium chloride solution at different pHs in water and/or methanol as solvent in separate experiments. Vaterite phase of calcium carbonate (CaCO3) has been synthesized by mixing calcium chloride and sodium carbonate in presence of para-aminobenzoic acid when water–methanol binary mixture was used as solvent. Vaterite phase of calcium carbonate crystallizes in P63/mmc, while that of calcite phase in R-3mc, respectively. Calcite phase of calcium carbonate exhibits rhombohedral morphology, while vaterite phase has spherical morphology.
09743626
Calcium carbonate--Vaterite--Chemical synthesis
QD31 JOU